O110 is the lowest material grade of gray cast iron defined in Sweden standard SS 14 01.
It is equal to HT100 in China, GG10 in DIN 1691, EN-GJL-100 in EN 1561, FC100 in JIS G5501, G10 in UNI 5007, 100 in BS 1452, FGG10 in NBN 830-01, T100 in AS 1830, SJG100 in NS11 100, or ISO 185/JL/100.
We summarize the following chemical composition and properties for SS 14 01 O110 gray cast iron according to EN-GJL-100 in European standard EN 1561.
The Chemical Composition for SS 14 01 O110 Gray Cast Iron:
This material grade is the lowest grade for grey cast iron, so normally, no need to require its chemical components. As long as it is grey cast iron, then it will be ok.
However, the chemical composition for reference as: C: 3.4-3.9, Si: 2.1-2.6, Mn: 0.5-0.8, P≤0.3, S≤0.15. This is only the composition to iron foundries for reference, and surely, it can not, and should not be taken as the inspection yard
General, Mechanical, Thermal and Technological Properties for SS 14 01 O110 Gray Cast Iron:
General
Property |
Temperature |
Value |
Density |
20.0 °C |
6.8 g/cm³ |
Mechanical
Property |
Temperature |
Value |
Comment |
Elastic modulus |
20.0 °C |
70 - 100 GPa |
|
Poisson's ratio |
23.0 °C |
0.21 [-] |
Typical for Grey Cast Iron |
Shear modulus |
23.0 °C |
41 GPa |
Typical for Cast Iron |
Tensile strength |
20.0 °C |
100 MPa |
|
100.0 °C |
120 MPa |
|
200.0 °C |
120 MPa |
|
300.0 °C |
115 MPa
Show Material materials with Tensile strength of 115 MPa |
|
400.0 °C |
115 MPa |
|
500.0 °C |
100 MPa |
|
600.0 °C |
60 MPa |
|
Thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
100.0 °C |
1.05E-5 1/K |
|
200.0 °C |
1.15E-5 1/K |
|
300.0 °C |
1.2E-5 1/K |
|
400.0 °C |
1.25E-5 1/K |
|
500.0 °C |
1.3E-5 1/K |
|
600.0 °C |
1.3E-5 1/K |
|
Melting point |
|
1127 - 1204 °C |
Typical for Grey Cast Iron |
Specific heat capacity |
200.0 °C |
460 J/(kg·K) |
|
Thermal conductivity |
20.0 °C |
60 W/(m·K) |
|
Technological properties
Processing methods: sand casting |