AISI 1016 SAE UNS G10160
Carbon Steel Foundry
Steel foundry in China for producing
AISI 1016 SAE UNS G10160 Carbon Steel castings. The followings are
this material's chemical composition, physical and mechanical
properties and equivalent material grades.
The following
datasheet provides an overview of AISI 1016 carbon steel.
Chemical
Composition
The chemical
composition of AISI 1016 carbon steel is outlined in the following
table.
|
Element |
Content
(%) |
|
Iron,
Fe |
98.13-99.58 |
|
Manganese, Mn |
0.60-0.90 |
|
Carbon,
C |
0.12-0.18 |
|
Sulfur,
S |
≤ 0.050 |
|
Phosphorous, P |
≤ 0.040 |
Physical Properties
The following
table shows the physical properties of AISI 1016 carbon steel.
|
Properties |
Metric |
Imperial |
|
Density |
7.87
g/cm3 |
0.284
lb/in³ |
Mechanical Properties
The mechanical
properties of cold drawn AISI 1016 carbon steel are displayed in the
following table.
|
Properties |
Metric |
Imperial |
|
Tensile
strength |
420 MPa |
60900
psi |
|
Yield
strength |
350 MPa |
50800
psi |
|
Bulk
modulus (typical for steel) |
140 GPa |
20300
ksi |
|
Shear
modulus (typical for steel) |
80.0
GPa |
11600
ksi |
|
Elastic
modulus |
190-210
GPa |
27557-30458 ksi |
|
Poisson's ratio |
0.27-0.30 |
0.27-0.30 |
|
Elongation at break (In 50 mm) |
18.00% |
18.00% |
|
Reduction of area |
40.00% |
40.00% |
|
Hardness, Brinell |
121 |
121 |
|
Hardness, Knoop (converted from Brinell hardness) |
140 |
140 |
|
Hardness, Rockwell B (converted from Brinell hardness) |
68 |
68 |
|
Hardness, Vickers (converted from Brinell hardness) |
126 |
126 |
|
Machinability (based on AISI 1212 steel as 100 machinability.
The machinability of Group I bar, rod, and wire products can
be improved by cold drawing.) |
70 |
70 |
Thermal Properties
The thermal
properties of AISI 1016 carbon steel are given in the following
table.
|
Properties |
Metric |
Imperial |
|
Thermal
conductivity (estimated based on similar materials) |
51.9 W/mK |
360 BTU
in/hr.ft².°F |
Other Designations
Equivalent
materials to AISI 1016 carbon steel are given in the following
table.
|
ASTM
A108 |
ASTM
A29 |
ASTM
A510 |
ASTM
A513 |
|
ASTM
A548 |
ASTM
A549 |
ASTM
A576 |
ASTM
A659 |
|
SAE
J403 |
SAE
J412 |
SAE
J414 |
ASTM
A545 |
|
MIL
SPEC MIL-S-866 |
|
|
|
|
|
|
|
|
Applications
AISI 1016
carbon steel is used in cold forming operations such as extrusion,
heading and upsetting.